学术报告信息一则(202106):镁合金激光表面重熔过程中的晶粒细化行为

来源: 时间:2021-07-01 10:42:26 作者: 点击:

报告题目:镁合金激光表面重熔过程中的晶粒细化行为

报告人:邱冬 教授

主持人(邀请人): 王慧远 教授

报告时间:20217214:00-15:00

报告地点:腾讯会议 会议ID721 856 033

主办单位:汽车材料教育部重点实验室,9001cc.s金沙登录

报告摘要:Columnar grains are normally favoured with the high cooling rate and steep thermal gradient in welding and laser-based additive manufacturing. In this study, we demonstrate that fine, fully equiaxed grains can be achieved in Mg-3Nd-1Gd-0.5Zr (EV31) alloy by laser surface remelting. The grains in the melt pool are remarkably refined from 74 μm to 3.5 μm, which can be attributed to the constitutional supercooling delivered by Zr solute in combination with the high thermal undercooling imposed by laser surface remelting. This novel finding could be applied for the control of grain morphology and alloy design for future additive manufacturing applications of Mg alloys.

报告人简介:Dong Qiu,男,19801月生,澳大利亚皇家墨尔本理工大学(RMITSenior Lecturer2005年从清华大学获得工学博士学位后,前往澳大利亚昆士兰大学先后以UQ Postdoc FellowAustralian Research Fellow的身份从事镁合金、铝合金、锌合金以及铁素体/奥氏体钢等多种工程合金凝固过程中高效晶粒细化剂的开发。2015年被皇家墨尔本理工大学(RMIT)聘为校长特聘高级研究员,开始介入金属3D打印(增材制造)领域,现在主要从事适合增材制造特点的新型工程合金的设计与开发,以及对3D打印过程中微观组织的调控与优化。以主要参与人的身份共获得4次澳大利亚自然科学基金(ARC Discovery Project)和1次应用创新基金(ARC Linkage Project)的资助,发表了86篇经同行评议的期刊论文,其中包括1篇以共同一作的身份发表在Nature上,以及17篇发表在国际物理冶金领域知名期刊Acta Materialia上,在Scopus搜索引擎上论文被引用总数达2300余次,H因子为28。现担任物理冶金学报(Metallurgical and Materials Transaction A)审稿委员会委员(key reader),澳大利亚自然科学基金评审专家,2017年被吉林大学聘为“唐敖庆”讲座教授。


© 版权所有:中国·金沙-www.9001cc.scom|官方网站-登录入口

地址:吉林省长春市人民大街5988号

邮编:130022

电话:0431-85094375

E-mail:cailiao@jlu.edu.cn

XML 地图

请升级浏览器版本

你正在使用旧版本浏览器。请升级浏览器以获得更好的体验。